环氧地坪漆起水泡多發生在一樓或地下室，有時二樓以上也時有發生，环氧地坪漆起水泡一般在施工後不久就發現，有的上午鋪貼的环氧地坪漆下午就有水泡。水泡由小到大，不斷開展，開展到一定程度後中止。氣溫越高，水泡就越容易發生，開展的速度也越快。水泡形狀各異，其大小不一。
Epoxy floor paint blisters often occur on the first floor or basement, sometimes on the second floor or above. Epoxy floor paint blisters are usually found shortly after construction, and some morning epoxy floor paint blisters in the afternoon. Blisters develop from small to large and continue to a certain extent. The higher the temperature is, the quicker the bubble is, and the faster it develops. The shapes of vesicles vary and vary in size. 水泡的發生與施工區域沒有明顯的聯系，同一區域有的嚴峻，有的較輕，有的無缺。同一小組操作，同一資料施工的环氧地上層，有的起水泡，有的無缺，闡明水泡是多種要素構成的。 起水泡的緣由，是我們關懷的一個問題，剖開水泡發現，泡內都富含水分或炎黃色液體，环氧地上層與底層脫離，粘在底層上的膠結料被拉成峰窩狀，依照“物理學”解說，在盛有液體的密閉容器內，液體蒸騰，構成飽和狀態的三條曲線的溫度與壓力聯系。
There is no obvious connection between the occurrence of blisters and the construction area. Some of them are severe, some are light and some are indispensable in the same area. The same group operation, the same data construction of the epoxy overground layer, some blisters, some absent, clarify that blisters are composed of a variety of elements. The cause of bubbles is a problem we care about. When we open the bubbles, we find that the bubbles are rich in water or yellow liquid. The upper layer of epoxy resin separates from the bottom layer. The cementing materia环氧地坪l adhering to the bottom layer is pulled into peaks and nests. According to the explanation of "physics", in the closed con彩色沥清地坪tainer containing liquid, the liquid transpires and forms a saturated state. The relation between the temperature and pressure of the three curves.
很多區域在酷熱的夏日地上的極點輻射熱可達70.C左右，在這樣的高溫下，环氧膠結料現已軟化粘力大大下降，因此就形同向輪胎內漸漸鼓氣相同，使环氧地上層中鼓起瞭大包，將膠結料被拉成蜂窩狀；其間沒有起水泡的有些环氧層和地上有些沾不結實，細心觀測接觸有些，也會發現有無法固化的有些，緣由是环氧有潮氣不能固化。
In many areas, the pole radiation heat of the ground in the hot summer can reach about 70.C. Under such high temperature, the epoxy cementing material has softened the adhesive force greatly, so it is the same as gradually blowing into the tire, making the epoxy ground layer bulge up a large package, pulling the cementing material into a honeycomb shape; there are some rings without blistering. Oxygen layer and ground are not solid, carefully observed contact with some, you will find that some can not be cured, because epoxy moisture can not be cured.