地坪廠傢講环氧地坪表面有刷痕如何解決

我們在地下停車場停車的時候也應該都會發現停車場的地面是比較平整的。並且光澤度也是很好看的。其實現在這都是使用瞭环氧地坪，环氧地坪不僅僅使用在地下車庫，在一些運動的場地、咖啡館等大型的場所也有使用。我們一般都是直接找施工團隊直接進行施工，但是在施工的時候可能會發現這樣的問題，比如說會有一些刷痕的存在，我們大傢選擇环氧地坪的目的就是想要一個光澤度好的地面，所以這個問題可以說是一個致命的缺陷，那麼我們在施工的時候應該怎麼去做才能避免和解決這種情況呢？下面我們就來詳細的介紹。
When we park in the underground parking lot, we should also find that the ground of the car park is relatively smooth. And the gloss is pretty good. In fact, this is the use of epoxy flooring, epoxy flooring is not only used in the underground garage, but also in some sports venues, cafes and other large places. We usually find the construction team directly to carry out the construction, but during the construction, we may find such problems. For example, there will be some brush marks. The purpose of choosing epoxy floor is to have a glossy surface. So this problem can be said to be a fatal defect. What should we do in the construction process to avoid and solve this situation? Next we will give a detailed introduction.
刷痕產生的原因：
Causes of brush marks:
A、施工原因：施工方法錯誤，塗料攪拌後施工時間過長，滾刷均勻，塗層薄厚控制不到位。
A. Construction reasons: incorrect construction method, long construction time after mixing, even rolling brush, poor control of coating thickness.
B、工具原因：滾筒質量不合格，滾筒表面處理有誤。
B, tool reason: drum quality is not qualified, roller surface treatment is wrong.
C、塗料本身的原因：主要是塗料的流平性差，塗料的粘度過高。有觸變性的填料或助劑。
C, paint itself: mainly due to poor levelling of paint and excessive viscosity of coatings. Thixotropic filler or auxiliaries.
解決的方法：
Solution:
A、註意施工方法，塗料的熟化時間不要過長。滾筒的二端到圓角，塗層的一遍厚度盡可能不要小於0.15mm。
A, pay attention to the construction method, an环氧地坪d the curing time of the paint should not be too long. The two ends of the drum to the fillet, the thickness of the彩色沥清地坪 coating should not be less than 0.15mm as much as possible.
B、買好一點的滾筒，滾筒使用前用膠帶處理一下滾筒表面
B, buy a little roller, use the tape to handle the roller surface before using the drum.
C、塗料的原因，增加塗料的流平性，降低塗料的粘度，盡可能減少有觸變性的填料和助劑，特別要註意墻面塗料的流平劑用在环氧地坪塗料的現象。
C. The causes of coatings, increase the leveling of coatings, reduce the viscosity of coatings, and minimize thixotropic fillers and additives. Particular attention should be paid to the phenomenon that leveling agents of wall coatings are used in floor coatings.