耐磨环氧地坪漆冬季該如何防止龜裂

环氧地坪冬季最常見的龜裂問題，是因為环氧耐磨地坪漆廠傢在進行施工中，施工間隔過短，环氧地坪漆不配套，环氧地坪漆塗層之間過厚或者因為材料攪拌不均勻等原因所導致的，其實造成龜裂問題出現的原因在專業的地坪漆施工師傅手中都是可以成功避免的，其中最主要的是在施工前和施工中做好預防措施。
The most common cracking problem of epoxy floor in winter is caused by the short construction interval, incomplete floor paint, excessive thickness between floor paint coatings or uneven mixing of materials in the construction of epoxy wear-resistant floor paint manufacturers. In fact, the causes of cracking problem are professional floor paint builders. Fuzhong can be successfully avoided, the most important is to do a good job in the construction of precautions before and during the construction. 在冬季低溫下，地坪漆接觸混凝土被冷卻，反應熱及時散發，會使固化時間變長，而环氧地坪漆固化時間變長就會使得塗層施工之間的間隔需要延長，而有些环氧耐磨地坪漆廠傢為瞭趕進度，沒有等底漆幹透就貿然進行第二塗層的施工，最後導致兩層塗膜內外伸縮力不一致導致開裂。在地坪漆施工過程中，一定要把握好每層环氧地坪漆的厚度，尤其在冬季低溫下，地坪塗料的固化時間長，過厚的地坪材料越難幹。 對於已經有龜裂現象的地坪地面也要分情況進行修復，隻是輕微龜裂的地面，在保證材料不沖突的情況下，再滾塗一遍面漆覆蓋就可以瞭，而有明顯裂紋的龜裂現象，就需要环氧耐磨地坪漆廠傢先用环氧中塗進行填充修補再滾塗一遍面漆。
At low temperatures in winter, floor paint contact印花地坪 with concrete is cooled, and the reaction heat is released in time, which will make the curing time longer, while the curing time of epoxy floor paint will make the interval bet彩色沥清地坪ween coating construction needs to be extended, and some epoxy wear-resistant floor paint manufacturers in order to catch up with the progress, without waiting for the primer to dry through the second coating. The construction of the layer finally leads to the two layers of paint film internal and external expansion force inconsistency leading to cracking. In the process of floor paint construction, we must grasp the thickness of each layer of epoxy floor paint, especially in winter low temperature, the floor paint solidification time is long, the thicker the floor material is more difficult to dry. For the ground that has cracks, it should be repaired according to different conditions. Only slightly cracked ground can be repaired by rolling over the top coat once more under the condition of guaranteeing no conflict of materials. Coat the top coat.