機械磨損，即是印花地坪當水泥地面和工業廠房环氧地坪被反復磨損，淹沒和沖擊而造成的損壞。然而混凝土的機械磨損就是當混凝土受反復的機械摩擦時，最先被磨損的是最表面的硬化水泥漿體層或者是水泥砂漿面層。因為混凝土的強度，硬度，特別是其面層的強度、硬度是據頂混凝土耐磨性的最重要的一點，混凝土的機械磨損會大大降低其面層的耐磨性能。
Mechanical wear is the damage caused by repeated wear, submergence and impact of cement floors and industrial plant floors. However, the mechanical wear of concrete is when the concrete is subjected to repeated mechanical friction, the first wear is the hardened cement paste layer or cement mortar surface layer. Because the strength and hardn彩色沥清地坪ess of concrete, especially the strength and hardness of its surface layer is the most important wear resistance of the top concrete, the mechanical wear of concrete will greatly reduce the wear resistance of its surface layer. 因為混凝土是同時具備泌水性和離析性的，水泥漿和細的顆粒容易浮在表面，形成一個比較薄弱的面層，然而，這就是混凝土耐磨損的最薄弱的环節。在混凝土施工之前，我們必須要等到泌水停止後再將浮漿清除，然後抹平表面，以有效減少浮漿層。養護，也是环氧地坪施工的一個重要事項，合理的養護地坪，可大大增加地坪的使用年限，我們也建議可以適當延長養護時間，保證表面層有足夠的強度。
Because concrete is both bleeding and segregation, cement slurry and fine particles are easy to float on the surface, forming a relatively weak surface, however, this is the weakest link in the wear resistance of concrete. Before concrete construction, we must wait until the bleeding stops to remove the floating slurry, and then smooth the surface to effectively reduce the floating slurry layer. Maintenance is also an important issue in floor construction. Reasonable maintenance of the floor can greatly increase the service life of the floor. We also suggest that the maintenance time can be properly extended to ensure that the surface layer has sufficient strength.
降低水灰比，摻加高效減水劑、矽灰等都是對提高混凝土的強度和密度有良好作用的措施。在要求高耐磨的性的機場地坪，工業廠房地坪等的面層混凝土中，我們還可以適當的加入一些金剛砂，金屬骨料等耐磨的材料，目的是要提高水泥地坪的機械強度和耐磨損性能。混凝土密封固化劑就屬於這類型的產品
Reducing water cement ratio, adding superplasticizer and silica fume are all good measures to improve the strength and density of concrete. In order to improve the mechanical strength and wear resistance of cement floors, some wear resistant materials such as diamond and metal aggregate can be added to the surface concrete of airport floors and industrial plant floors which require high wear resistance. The concrete seal curing agent belongs to this type of product.