揭示环氧樹脂防腐地坪功能以及施工工藝

在許多的公共場合都能看到环氧樹脂防腐环氧地坪漆的身影,因其具有許多優點,耐腐蝕區等等優點,受到瞭工業的喜愛,對於环氧樹脂防腐环氧地坪漆功能以及施工工藝現在就讓我們一起來瞭解一下相關知識,希望通過以下的介紹,能夠對你有所幫助。
In many public places can see the figure of epoxy resin anticorrosive floor paint, because it has many advantages, corrosion resistance zone and other advantages, by the industry favorite, for epoxy 彩色沥清地坪resin anticorrosive floor p透水地坪aint function and construction technology now let us together to understand the relevant knowledge, I hope that through the following introduction, can you Help.
环氧樹脂地坪漆防腐功能：
Epoxy resin floor paint anticorrosive function:
1、防腐地坪漆為三組份漆,適合防腐罐、重型機械表面處理及化工企業易腐蝕區域的地坪,石油工業的防腐工程及污水池化學池等。抗滲透性強,耐強酸、堿、鹽及各種有機溶劑,表面硬度高,致密性好。本漆分為A、B兩組份,其中A組為环氧胺類固化劑,B組為环氧色漆、玻璃粉組成。該漆耐強酸堿、耐海水、鹽霧及各類化學介質腐蝕、附著力強、耐磨、耐沖擊、、防塵等。主要適用於化工廠、輸送管道、電鍍廠、海洋設備等塗裝。
1. Anti-corrosion floor paint is a three-component paint, suitable for anti-corrosion tanks, heavy machinery surface treatment and chemical industry corrosion-prone areas of the floor, petroleum industry anti-corrosion engineering and sewage tank chemical pool. It has strong resistance to penetration, strong acid, alkali, salt and various organic solvents. The surface hardness is high and the compactness is good. The paint is divided into two components A and B, of which group A is epoxy amine curing agent, group B is epoxy paint, glass powder composition. The paint is resistant to strong acid and alkali, seawater, salt spray and various chemical media corrosion, strong adhesion, wear resistance, impact resistance, dust and so on. It is mainly applied to chemical plant, transportation pipeline, electroplating plant, marine equipment and so on.
2、優良的附著力:环氧樹脂地坪塗料具有許多羥基及醚鍵,所以能與底材料吸附。而且环氧樹脂固化時體積收縮率低,故漆膜對金屬,陶瓷,玻璃,混凝土,木材等極性底材均有優良的附著力。
2. Excellent adhesion: Epoxy floor coating has many hydroxyl and ether bonds, so it can be adsorbed with the substrate. And the volume shrinkage of epoxy resin curing is low, so the film has excellent adhesion to metal, ceramics, glass, concrete, wood and other polar substrates.
3、环氧樹脂地坪對濕面有一定的潤濕力,尤其在使用聚酰胺樹脂作固化劑時,可制成水下施工塗料,能排擠物體表面的水而塗佈,可用於水下結構的搶修和水下結構的防腐蝕施工。
3. Epoxy resin floor has a certain wetting force on the wet surface. Especially when polyamide resin is used as curing agent, it can be made into underwater coating, which can expel water from the surface of the object and be used for rush repair of underwater structures and anti-corrosion construction of underwater structures.
4、环氧樹脂地坪本身的分子不高,能與各種固化劑配合制造無溶劑,高固體分粉末塗料及水性塗料,符合环保要求,並能獲得厚膜塗層。
4. Epoxy floor itself is not high in molecule, can be used with a variety of curing agents to produce solvent-free, high solid powder coatings and water-based coatings, in line with environmental requirements, and can obtain thick film coating.
5、环氧樹脂地坪含有环氧基及羥基兩種活潑基團,能與多元胺,聚酰胺樹脂,酚醛樹脂,氨基樹脂,多異氰酸酯等配合,制成多種塗料,既可常溫幹燥,可可高溫烘烤,以滿足不同的施工要求
5. Epoxy resin floor contains two active groups of epoxy group and hydroxyl group. It can be combined with polyamine, polyamide resin, phenolic resin, amino resin, polyisocyanate and so on to make a variety of coatings. It can be dried at room temperature and baked at high temperature to meet different construction requirements.
环氧樹脂地坪
Epoxy floor
环氧樹脂地坪漆施工工藝的方法：
The construction technology of epoxy floor paint:
1.一種环氧地坪漆施工方法,其特征在於,包括如下步驟:
1. the construction method of epoxy floor paint is characterized by the following steps:
1.封閉底漆施工:用刷塗、輥塗或噴塗的方法施工封閉地坪漆底漆一道至兩道,兩道之間的間隔時間在8h以上,但不能大於48h。對於舊地面,應增加一道底漆。底漆施工時應註意塗佈均勻,塗膜無明顯的厚度差異,防止漏塗。用輥塗法施工應註意餘料堆積情況。底漆封閉不完全(漏塗)時,會發生附著不牢、塗膜起泡等現象。
1. Closed primer construction: Use brush, roll or spray method to apply one or two closed floor primer, the interval between the two primers is more than 8 hours, but not more than 48 hours. For old ground, a primer should be added. Attention should be paid to uniform coating when priming is applied, and no obvious difference in thickness is observed to prevent leakage. Attention should be paid to the accumulation of residual materials by roller coating method. When the primer is not fully sealed (leak coating), it will cause adhesion, coating and bubbling.
2.膩子修補:對水泥基層存在的凹坑,用商品环氧膩子或用底漆和細石英砂配置的环氧砂漿填平,在固化成膜後打磨平整。推薦查看:產品展示
2. Putty repairing: The pits in the cement base are filled with commercial epoxy putty or epoxy mortar with primer and fine quartz sand, and then polished after curing. Recommended view: product display
3.中層塗料施工:對於厚膜型塗料,中層塗料施工時可采用鏝刀鏝塗。由於塗料中使用的石英砂較多,一般情況下刮塗後塗膜不會出現明顯刮刀痕跡,但如果石英砂加入量過大,刮痕明顯時應輥壓一次。塗裝間隔如果大於48h,應進行打磨後再進行下道塗料的施工,以保證層間黏結力。
3. medium coating construction: for thick film coatings, trowel trowel can be used for middle coating construction. Due to the use of more quartz sand in the paint, the film will not appear obvious scratch marks under normal circumstances, but if the addition of quartz sand is too large, scratch obvious should be rolled once. If the coating interval is greater than 48 hours, the next coating should be applied after grinding to ensure interlaminar adhesion.
4.面塗料施工:根據环氧耐磨地坪塗料的種類,面塗料可以采用刷塗或刮塗施工。對於厚膜型塗料,按配比要求將兩組份塗料混合均勻,待熟化後使用1mm刮板刮塗塗料。刮塗時應盡量保持厚膜均勻,無漏塗現象,無明顯餘料。刮塗時,刮刀的移動速度應均勻,刮刀與地面平面夾角為30°左右,以保證塗膜厚度。刮塗道數根據厚度要求而定。普通环氧塗料則可以采取刷塗方法施工。面圖料施工時兩道之間的間隔時間應在18h以上,但不能大於48h。配置好的塗料應盡快用完,以防止塗料的黏度升高,塗料中的氣泡難於排出。
4. Surface coating construction: According to the type of epoxy wear-resistant floor coating, the surface coating can be brushed or scraped. For thick film coatings, mix the two components evenly according to the proportion requirements, and use 1mm scraper coating after curing. During scraping, thick film should be kept as uniform as possible without any leakage. When scraping, the moving speed of the scraper should be uniform, and the angle between the scraper and the ground plane should be about 30 degrees to ensure the film thickness. The number of scraper passes depends on the thickness requirements. Ordinary epoxy coatings can be constructed by brush method. The interval between the two roads should be above 18h, but not more than 48h. The finished coatings should be used up as soon as possible to prevent the paint from rising and the bubbles in the paints are difficult to discharge.
5.打蠟養護:面塗料施工完,並完全固化後(一般應在面塗料施工24h以上),進行打蠟養護,兩周後可驗收使用。
5. Wax curing: After the surface coating is finished, and completely cured (generally should be more than 24 hours of surface coating construction), wax curing, two weeks after acceptance of use.