廠傢揭示不同环氧地坪塗料厚度差異有什麼好處

环氧地坪是一種高強度、耐磨損、美觀的地面材料，具有無接縫、質地堅實、耐藥品性佳、防腐、防塵、保養方便、維護費用低廉等優點。可根據不同的用途要求設計多種方案，下面以此分析环氧地坪材料的厚度差異以及一些施工方法：
Epoxy floor is a kind of high-strength, wear-resistant, beautiful ground material, with seamless, solid texture, good resistance to antisepsis, dust, easy maintenance, low maintenance costs and other advantages. Various schemes can be designed according to different usage requirements. The following is an analysis of the thickness differences of epoxy floor materials and some construction methods:
环氧地坪材料的厚度差異
Thickness difference of epoxy floor material
1、环氧平塗环氧地坪：最為普通的环氧地坪材料的一種，也叫薄層环氧地坪。因為其特點是薄，所以其塗層較薄。底塗層一般施工下都是在1毫米之下，近幾年的工程厚度多在0.2-0.5毫米之間。面層的厚度約為0.1毫米，非常的薄。也有人采用噴塗的工藝進行施工，可將厚度更加的降低。
1, epoxy floor coating: one of the most common epoxy floor materials, also known as thin epoxy floor. Because its characteristics are thin, its coating is thinner. The bottom coating is generally under 1 mm under construction, in recent years the engineering thickness is mostly between 0.2-0.5 mm. The thickness of the surface is about 0.1 millimeters, very thin. Some people use spraying technology to carry out the construction, which can further reduce the thickness.
2、环氧砂漿环氧地坪：其塗層相對厚度較高。中塗采用的砂漿刮塗進行1-3毫米的施工，面層同一般的地坪材料施工工藝，厚度保持在0.1毫米左右。總塗層的厚度保持在1-10毫米之間。
2, epoxy mortar floor: the coating has relatively high thickness. Slurry scraping used in the middle coating for 1-3 mm construction, the surface of the same general floor material construction technology, the thickness of about 0.1 mm. The total coating thickness is kept between 1-10 millimeters.
3、环氧自流平地坪材料：也叫流展地坪、环氧自流平砂漿地坪，因為其是自流平的緣故，所以厚度較前兩者較高。膩子層印花地坪刮塗在1-3毫米是常見的情況。面層在自流平的情況下維持在0.7-1毫米之間，相比之前的要厚瞭不少。塗層總厚度保持在1.5-10毫米左右。
3. Epoxy self-leveling floor materials: also known as flow exhibition floor, epoxy self-leveling mortar floor, because it is self-leveling, so the thickness is higher than the first two. Putty layer scraping on 1-3 mm is a common case. The surface layer is maintained at 0.7-1 mm in self leveling condition, much thicker than before. The total thickness of the coating is about 1.5-10 mm.
4、环氧防靜電地坪：其施工的時候添加瞭導電通路這一層。其他施工方式基本與普通地坪一樣。總厚度一般情況下是0.2-0.5毫米，建議不要超過1毫米。
4, epoxy anti-static floor: when the construction time, this layer is added. Other construction methods are basically the same as ordinary floors. The total thickness is 0.2-0.5 mm in general. It is recommended not to exceed 1 mm.
环氧地坪材料施工方法
Construction method of epoxy floor material
一、环氧地坪表面的處理
1. Surface treatment of epoxy floor.
1、新竣工的工業地坪必須經過一定的養護後方可施工，約28天。
1. The newly completed industrial floor must be constructed after maintenance for about 28 days.
2、清除表面的水泥浮漿、舊漆以及粘附的垃圾雜物。
2, remove the surface of cement slurry, old paint and adhesion of garbage debris.
3、徹底清除表面的油污。
3, thoroughly remove the surface oil pollution.
4、清除積水，並使潮處徹底幹燥。
4, clear up the water and make the tide completely dry.
5、表面的清潔需用無塵清掃機及大型吸塵器來完成。
5, surface cleaning must be done wi透水地坪th dust-free sweeper and large vacuum cleaner.
6、平整的表面允許空隙為2～2.5mm，含水量在6％以下，PH值6～80。
6. The smooth surface allows 2 to 2.5mm voids, and the water content is below 6%, pH 6~80.
7、地坪表面的打毛，需用無塵打磨機來完成，並用吸塵器徹底清潔。
7. The surface of the floor must be finished with a dust-free grinding machine and thoroughly cleaned with a vacuum cleaner.
8、對地坪表面的洞孔和明顯凹陷處應用膩子來填補批刮，實幹後，打磨吸塵。
8. Use putty to fill and scrape holes and obvious depressions on the surface of the floor. After dry, grind and dust.
二、批刮兩道膩子
Two, batch scraping two putty.
1、在實幹(25℃，約4小時)今後的底漆外表選用兩道批刮膩子的辦法，以保證地坪的耐磨損、耐壓性、磕碰、水、礦物油、酸堿溶液等功能，並調整地上平坦度。
1. In the dry (25 degrees Celsius, about 4 hours) the future primer surface selection of two batches of the method of scraping putty to ensure that the floor wear resistance, pressure resistance, knock, water, mineral oil, acid and alkali solution and other functions, and adjust the surface flatness.
2、用100～200意圖石英砂和环氧批刮料，作為第1道膩子，要充沛拌和均勻、刮平，此道首要用於增強地上的耐磨及抗壓功能。
2. Use 100-200 intent quartz sand and epoxy batch scraping materials as the first putty, to mix well and scrape flat, this way is primarily used to enhance the ground wear and compression resistance.
3、用砂袋式無塵翻滾磨砂機打磨第1道膩子，並吸塵清洗。
3, use sandbag type dust-free roller grind machine to polish first putty, and dust cleaning.
4、用200—270意圖石英砂和环氧批刮料，作為第1道膩子，要充沛拌和均勻、刮平，此道首要用於增強地上的耐磨及平坦度。
4. Use 200-270 intent quartz sand and epoxy batch scraping material as the first putty, to mix well and scrape flat, this way is mainly used to enhance the ground wear resistance and flatness.
5、用砂袋式無塵翻滾磨砂機打磨第2道膩子，並吸塵清洗。
5, use sandbag type dust-free roller grind machine to polish second putty, and dust cleaning.
6、兩道膩子實幹今後，如有麻面、裂縫處應先進行修補，然後用平板砂光機進行打磨，使其平坦，並吸塵清洗。
6. Two putty dry in the future, if there are hemp surface, cracks should be first repaired, and then use flat sander to grind, make it flat, and vacuum cleaning.
7、石英砂運用目數由現場工程師根據地上具體狀況斷定。
7. The number of quartz sand used is determined by the specific conditions of the field engineer on the ground.