环氧地坪表面的塗膜，因塗裝質量不良，或在使用過程在逐漸老化、脫落、開裂，或因長期磨損造成塗膜破壞，需要重新塗裝時，必須將損壞塗層去除。去除环氧地坪表面質量不良塗膜可采取以下方案：
The coating on the surface of epoxy floor must be removed when it needs to be repainted because of poor coating quality, gradual aging, shedding, cracking, or long-term wear and tear. To remove the poor quality of epoxy floor surface, the following solutions can be adopted:
將失效塗膜除去，而保留功能尚好的塗層再進行环氧地坪塗裝，這裡需註意，重新塗裝前必須弄槍原塗裝塗料的配套體系，嚴格按照塗料配套進行。檢查被保留塗膜確無缺陷後，去頂塗料品種。
Removal of the invalid coating film, and retain the good function of the coating and then epoxy floor coating, it should be noted here, before re-painting must be gun original coating system, strictly in accordance with the coating matching. After checking that the coating is not defective, remove the top coating varieties.
若底漆為环氧地坪塗料，可保留完好塗膜，上面需配套塗裝的塗料選擇范圍則較寬，大多數塗料都可以直接加塗。
If the primer is epoxy floor coatings, can retain intact film, the above coating needs to be coated with a wide range of coatings, most coatings can be directly applied.
完全將表面的塗膜去除，直至露出基材本體。當塗過漆的表面出現瞭腐蝕、起皮、起泡、開裂、起鱗或全面破裂的現象時，應把損壞的塗膜完全除去，直到露出裸露基體表面再重新塗裝。由於重新塗裝涉及塗料配套問題，如果是單組分环氧地坪丙烯酸、氯化橡膠等揮發幹燥塗料，則很容易出現咬底等問題，环氧环氧地坪加塗時一定要選擇合適的塗料。
The surface coating is removed until the substrate body is exposed. When corrosion, peeling, blistering, cracking, scaling or total cracking occur on the painted surface, the damaged film should be completely removed until the exposed substrate surface is re-coated. Because the re彩色沥清地坪-coating involves coating matching problems, if it is a one-component epoxy floor acrylic acid, chlorinat透水地坪ed rubber and other volatile dry coatings, it is easy to occur underbite and other issues, epoxy floor coating must be selected when the appropriate coating.